Group | Density (kg/m3) | MC (%) | σb (N/mm2) | Failure mode and number |
|---|---|---|---|---|
9L9P-Ma | 383 (0.70) | 10.6 (3.5) | 18.6 (7.3) | Bending: 8 |
9L9P-Mi | 382 (1.06) | 10.0 (6.6) | 10.3 (10.8) | Bending: 8 |
7L7P-Ma | 382 (1.39) | 10.7 (4.8) | 21.0 (14.0) | Bending: 8 |
7L7P-Mi | 387 (1.25) | 10.1 (2.5) | 9.3 (12.1) | Bending: 8 |
5L7P-Ma | 391 (2.56) | 10.6 (5.8) | 28.9 (9.0) | Bending: 7, Bending + Shear: 1 |
5L7P-Mi | 385 (1.45) | 10.6 (4.4) | 4.8 (11.7) | Bending: 8 |
5L5P-Ma | 394 (0.67) | 9.4 (3.8) | 26.9 (13.9) | Bending: 6 |
5L5P-Mi | 381 (0.71) | 9.7 (3.6) | 9.1 (11.4) | Bending: 6 |
3L4P-Ma | 408 (1.44) | 8.0 (1.6) | 25.2 (3.0) | Shear: 6 |
3L4P-Mi | 390 (1.84) | 10.6 (5.2) | 7.0 (8.5) | Bending: 6 |
3L3P-Ma | 398 (2.71) | 10.7 (5.2) | 30.7 (16.5) | Bending: 6 |
3L3P-Mi | 401 (4.18) | 10.4 (4.4) | 4.4 (8.9) | Bending: 6 |